5XXX

EN AW 5052
CHEMICAL COMPOSITION (%)
SiFeCuMnMgCrZnTiAl
0,250,40,10,12,2-2,80,15-0,350,1-Balance
EXTRUDED WIRE ROD
TemperWall Thickness (t)
(mm)		Tensile Strength
(Mpa)		Yield Strength
(Mpa)		Elongation (%)Hardness (HB)
DSMinMaxMinMaxMinMin
F,H112AllAll170-70-1347
0,H111AllAll17023070-1545
EXTRUDED PIPE
TemperWall Thickness (t)
(mm)		Tensile Strength
(Mpa)		Yield Strength
(Mpa)		Elongation (%)Hardness (HB)
MinMaxMinMaxMinMin
F,H112Hepsi170-70-1347
0,H111Hepsi17023070-1545
EXTRUDED PROFILE
TemperWall Thickness (t)
(mm)		Tensile Strength
(Mpa)		Yield Strength
(Mpa)		Elongation (%)Hardness (HB)
MinMaxMinMaxMinMin
F,H112Hepsi170-70-1347


D = Diameter of the round bar
S = Distance between two parallel sides for square and hexagonal bar, thickness for rectangular bar.
F light processing: property values are for information only.
CHARACTERISTIC FEATURES
It is a material with high anodizing ability. This alloy, which has high welding capability, has a very high resistance to corrosive environments, especially in the marine sector.

PRODUCTION TYPES
Production is possible for Sheet, Roll, Lama types.

AREAS OF USE
It is consumed in areas such as maritime and space industry.
EN AW 5083
CHEMICAL COMPOSITION (%)
SiFeCuMnMgCrZnTiAl
0,40,40,10,4-1,04,0-4,90,05-0,250,250,15Balance
EKSTRÜZE EDİLMİŞ TELLİK ÇUBUK
TemperWall Thickness (t)
(mm)		Tensile Strength
(Mpa)		Yield Strength
(Mpa)		Elongation (%)Hardness (HB)
DSMinMaxMinMaxMinMin
F≤ 200
200< D ≤ 250		≤ 200
200< S ≤ 250		270
260		-
-		110
100		-
-		10
-		70
70
0,H111≤ 200≤ 200270-110-1070
H112≤ 200≤ 200270-125-1070
EXTRUDED PIPE
TemperWall Thickness (t)
(mm)		Tensile Strength
(Mpa)		Yield Strength
(Mpa)		Elongation (%)Hardness (HB)
MinMaxMinMaxMinMin
FHepsi270-110-1070
0,H111Hepsi270-110-1070
H112Hepsi270-125-1070
EXTRUDED PROFILE
TemperWall Thickness (t)
(mm)		Tensile Strength
(Mpa)		Yield Strength
(Mpa)		Elongation (%)Hardness (HB)
MinMaxMinMaxMinMin
FHepsi270-110-1070
H112Hepsi270-125-1070

D = Diameter of the round bar.
S = Distance between two parallel sides for square and hexagonal bar, thickness for rectangular bar.
F light processing: property values are for information only.

CHARACTERISTIC FEATURES
High weldability, very good corrosion resistance to sea water, high fatigue strength, good cold formability in soft temper form.

PRODUCTION TYPES
It is possible to produce for Sheet, Roll, Lama, rod, pipe types.

AREAS OF USE
It is used in areas such as shipbuilding, storage tanks, offshore masts, pressure vessels.
EN AW 5754
CHEMICAL COMPOSITION (%)
SiFeCuMnMgCrZnTiAl
0,40,40,10,52,6-3,60,30,20,15Balance
EXTRUDED WIRE ROD
TemperEt Kalınlığı (t)
(mm)		Çekme Mukavemeti
(Mpa)		Akma Mukavemeti
(Mpa)		Uzama (%)Sertlik (HB)
DSMinMaxMinMaxMinMin
F,H112≤ 150
150< D ≤ 250		≤ 150
150< S ≤ 250		180
180		-
-		80
70		-
-		12
-		47
47
0,H111≤ 150≤ 15018025080-1545
EXTRUDED PIPE
TemperEt Kalınlığı (t)
(mm)		Çekme Mukavemeti
(Mpa)		Akma Mukavemeti
(Mpa)		Uzama (%)Sertlik (HB)
MinMaxMinMaxMinMin
F,H112≤ 25180-80-1247
0,H111≤ 2518025080-1545
EXTRUDED PROFILE
TemperEt Kalınlığı (t)
(mm)		Çekme Mukavemeti
(Mpa)		Akma Mukavemeti
(Mpa)		Uzama (%)Sertlik (HB)
MinMaxMinMaxMinMin
F,H112≤ 25180-80-1247

D = Diameter of the round bar.
S = Distance between two parallel sides for square and hexagonal bar, thickness for rectangular bar.
F light processing: property values are for information only.

CHARACTERISTIC FEATURES
High corrosion resistance, very good weldability; especially resistant to industrial atmosphere and sea water. Suitable for cold forming, high fatigue strength, suitable for coating.

PRODUCTION TYPES
sheet, bar, pipe, tube, strip, wire, profile types.

AREAS OF USE
It is used in nuclear applications, ship and boat building, chemical and food industry, pressure and boiling vessels, vehicle bodies, road poles.